Metal silicate-silica-based polymorphous phosphors and lighting devices

ABSTRACT

Provided, among other things, is a phosphor according to the formula: 
 
[(BvSiO 3 ) x (Mv 2 SiO 3 ) y (Tv 2 (SiO 3 ) 3 ) z ] m .(SiO 2 ) n :Rε, X  (I) 
     wherein x, y and z are any value such that x+y+z=1; By is one or more divalent alkaline earth metals; Mv is one or more monovalent alkaline metals; Tv is one or more trivalent metal ions; Rε is one or more activators selected from Eu 2+  and Mn 2+ ; X is one or more halides; m is 1 or 0; and (i) n&gt;3 if m=1 and provides an amount of silica effective to host useful luminescence or (ii) n=1 if m=0.

This application claims the priority of the following cases filed Mar. 25, 2005: Ser. Nos. 60/665,458; 60/665,636; 60/665,456; and 60/665,457; and Ser. No. 60/684,373, filed May 25, 2005.

The present invention relates to metal silicate-silica-based, polymorphous phosphors, methods of making, and semiconductor lighting devices modified with the phosphors.

In lighting applications phosphors can be used to modify or manage the wavelength of light output. For example, with UV or blue light emitting diodes (LEDs) can be enhanced to produce visible light or less blue light by positioning phosphors along the emission pathway to convert light to longer wavelengths. Blue, green and red emitting phosphors can be used to modify UV to white light. Green and red emitting phosphors can be used to modify a blue output to white light. Yellow emitting phosphors can be mixed with light from a blue emitting diode or a blue emitting phosphor to create light of white chromaticity. The phosphors described here, when matched with appropriate light sources, can be used in such applications.

Near UV emitting solid state lighting devices incorporating semiconductor light sources (such as LEDs), hold the promise of producing light with sufficient efficiency that, with the light emission modified to the visible range with appropriate phosphors, they may be cost-effectively employed to provide a wide range of lighting devices for use in electronics as well as general illumination. The lattices of these semiconductor light emitting diode is typically InGaN-based doped by minor portions of magnesium to generate enough defects for radiation recombination of electrons and holes. For example, Nichia has made a 100 mW InGaN-based semiconductor light source designated NCCU033E, and an 85 mW GaN-based semiconductor light source designated NCCU001 E. To utilize these near UV light sources in lighting products, phosphors with the appropriate excitation and emission characteristics are needed.

For near UV-LED devices, phosphors are used to convert the primary emission wavelength from 360 to 420 nm to visible light, especially to produce white light. These phosphors can be categorized into red-emitting, green-emitting and blue-emitting components. There are some existing phosphors, developed for other applications, which have an excitation profile to enable visible emission. Green-emitting examples include (Ba_(1-x-y),Ca_(x)Sr_(y))₂(Mg_(1-z)Zn_(z))Si₂O₇:Eu; Ca₈Mg(SiO₄)₄C₁₂:Eu,Mn; Ba₂SiO₄:Eu Ba₂MgSi₂O₇:Eu; Ba₂ZnSi₂O₇:Eu, BaAl₂O₄:Eu; SrAl₂O₄:Eu; BaMg₂Al₁₆O₂₇:Eu; and Ca₈Mg(SiO₄)₄Cl₂:Eu,Mn. Blue-emitting examples include BaMg₂Al₁₆O₂₇:Eu; (Sr,Ba,Ca)₅(PO₄)₃Cl:Eu and Sr₄Al1₄O₂₅:Eu. These phosphors are fairly efficiently excited by near UV light in the wavelength ranging from 360 to 420 nm. Red-emitting examples include Y₂O₂S:Eu,Bi, Y₂O₃:Eu, Bi and 3.5MgO.0.5MgF₂.GeO₂:Mn.

However, some of these phosphors are not ideally suited for wavelength conversion and in many cases have low efficiency when excited by a typical UV LED wavelength of 400 nm. Phosphors which are engineered to have the desired emission characteristics and which possess an excitation profile ideally suited for UV LEDs, are still needed.

Certain heterogeneous divalent europium and manganese activated, metal halide-silica phosphors have been described (Lehmann, J. Elect. Soc. 22:748-52, 1975), but with no description of use. The phosphors, which were doped with europium or europium plus manganese, were described as “luminescent halides dispersed in small segregations inside of bigger and nonluminescent SiO₂ particles.” (Emphasis added.) According to the author, X-ray diffraction data “normally show only lines corresponding to the α-cristobalite modification of SiO₂. Whatever else is present must be either amorphous or in amounts too small to be detected by routine x-ray analysis (detectability limit: several %).” These phosphors have been described as being produced by firing in the presence of an excess of ammonium halide in a slightly reducing atmosphere. Attempts to reproduce this preparation method yielded explosions. The materials processed by the methods described below yielded product which XRD analysis has repeatedly shown to have a metal inosilicate and crystalline silica composition.

The metal silicate-silica-based, polymorphous phosphors are effectively used as wavelength converters with near UV or blue-emitting semiconductor or LED light sources. They can provide stable phosphors that are usefully excited with near UV, including red-emitting phosphors, pink-emitting phosphors, blue-emitting phosphors, and the like. Different phosphors of the present invention, or such phosphor(s) and other phosphors can be mixed to achieve different chromaticities, including white light.

EXEMPLARY EMBODIMENTS

A family of activated metal silicate-silica-based, polymorphous phosphors are believed to be useful for such applications. In one embodiment, the phosphors of the invention are according to the formula: [(BvSiO₃)_(x)(Mv₂SiO₃)_(y)(Tv₂(SiO₃)₃)_(z)]_(m).(SiO₂)_(n):Rε, X  (I) wherein By is one or more divalent metal ions; Mv is one or more a monovalent ions; Tv is one or more trivalent metal ions; x, y and z are any value such that x+y+z=1; RE is one or more activators selected from Eu²⁺ and Mn²⁺. X is one or more monovalent halides selected from F⁻, Cl⁻, Br⁻ or I⁻. RE is present, for example in an amount effective to provide luminescent emission. The value of m is 1 or 0. The value of n is >3 if m=1, and is such as to provide an amount of silica effective to host useful luminescence. The value of n is 1 if m=0. By, Mv and Tv are metal ions that support the formation of the metal silicates.

It is believed that where a mix of Mv and By, or Mv and Tv, or By and Tv, or Mv, By and Tv, is present, the Mv silicate, By silicate and Tv silicates are in separate crystalline phases. The metal silicate is believed to be in a separate phase from the silica (SiO₂)_(n). The phases are separate in that they can be detected in XRD data.

The metal silicate is present in an amount that supports formation of other crystals in the host materials. Useful amounts are believed to include, for example, amounts from 1-10% of the phosphor composition. n describes an amount of matrix silica, which can be 100% amorphous, 100% cristobolite, contain quartz, or a mixture anywhere in between. The value of n can be determined from a compositional analysis and XRD estimation of the amount of MSiO₃.

In one embodiment, By is an alkaline earth metal ion, such as one or more of ions of Be, Mg, Ca, Sr or Ba. In one embodiment, By is one or more of ions of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Zr, Nb, Mo, Ru, Rh, Pd, Ag, Cd, Ta, W, Re, Os, Ir, Pt, Au or Hg. In one embodiment, By is one or more of ions of Be, Mg, Ca, Sr, Ba, Mn, Co, Ni, Cu, Zn, Cd or Hg. In one embodiment, Tv is one or more ions of Al, Ga, In, Sc, Y or La. In one embodiment, Mv is one or more alkaline metal ions, such as Li, Na or K.

The composition can be very stable, in that it retains 85% or more, 86% or more, 87% or more, 88% or more, 89% or more, 90% or more, 91% or more, or 92% or more of its relative emission intensity after 400 hours at 85° C. in the presence of 85% relative humidity.

In certain embodiments, the mole percentage of Rε in the composition is 0.001% to 10% of silica (SiO₂) (or, in some embodiments, of formula components). In certain embodiments, the range of the mole percentage of Rε is from one of the following lower endpoints (inclusive) or from one of the following upper endpoints (inclusive). The lower endpoints are 0.001%, 0.01%, 0.02%, 0.05%, 0.1%, 0.2%, 0.5%, 1%, 2%, 3%, 4% and 5%. The upper endpoints are 0.01%, 0.02%, 0.05%, 0.1%, 0.2%, 0.5%, 1%, 2%, 3%, 4%, 5% and 10%. For example, the range can be 0.01% to 5%.

In certain embodiments, the mole percentage of X in the composition is 0.002% to 5% of silica (SiO₂) (or, in some embodiments, of formula components). In certain embodiments, the range of the mole percentage of Rε is from one of the following lower endpoints (inclusive) or from one of the following upper endpoints (inclusive). The lower endpoints are 0.002%, 0.01%, 0.02%, 0.05%, 0.1%, 0.2%, 0.5%, 1%, 2%, 3% and 4%. The upper endpoints are 0.01%, 0.02%, 0.05%, 0.1%, 0.2%, 0.5%, 1%, 2%, 3%, 4% and 5%. For example, the range can be 0.01% to 5%.

In certain embodiments, the mole percentage of BvSiO₃ and/or Mv₂SiO₃ and/or Tv₂(SiO₃)₃ is 0.1% to 40% of silica (SiO₂) (or, in some embodiments, of formula components). In certain embodiments, the range of the mole percentage of BvSiO₃ and/or MvSiO₃ and/or Tv₂(SiO₃)₃ is from one of the following lower endpoints (inclusive) or from one of the following upper endpoints (inclusive). The lower endpoints are 0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 0.7%, 1%, 2%, 5%, 10%, 15%, 20%, 30% and 40%. The upper endpoints are 0.2%, 0.3%, 0.4%, 0.5%, 0.7%, 1%, 2%, 5%, 10%, 15%, 20%, 30%, 40% and 50%. For example, the range can be 5% to 10%.

In certain embodiments, x=1. In certain embodiments, y=1. In certain embodiments, z=1. In certain embodiments, one or two of x, y and z are zero.

In certain embodiments, X is a halide and is 99.9% (molar) or more of a given halide, such as 99.9% (molar) or more chloride, or 99.9% (molar) or more iodide, or 99.9% (molar) or more bromide. X is generally present in an amount that charge neutralizes Rε.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1 (Ex. 1), 4 (Ex. 2), 5 (Ex. 3), 7 (Ex. 4), 8 (Ex. 5), 10 (Ex. 6), 11 (Ex. 7) and 12 (Ex. 8) show excitation and emission spectra of phosphors of the invention.

FIGS. 2 (Ex. 1) and 6 (Ex. 3) show stability data for phosphors of the invention.

FIGS. 3 (Ex. 1) and 9 (Ex. 5) show X-ray diffraction data for phosphors of the invention.

FIGS. 13 and 14 show light emitting devices.

FIG. 15 illustrates an exemplary layer structure for a near UV emitting semiconductor light source.

DETAILED DESCRIPTION OF THE INVENTION

The host material of the phosphors is believed to be polymorphous metal silicates and silica. The silica, SiO₂, constitutes the greater part of the host materials. The silica can be crystallized in cristobalite which is made from SiO₄ tetrahedral units fused together by sharing oxygen atoms. The crystal can have the space group of P4₃2₁2 of tetragonal system. The silica can also be present in quartz or amorphous forms. The metal silicates, BvSiO₃ and Mv₂SiO₃, are believed to be in the form of inosilicates in which tetrahedral polymerization is based upon (SiO₃), as in the pyroxene jadeite, NaAl[Si₂O₆], and double chain silicates with tetrahedral polymerization, as found in the amphilbole glaucophane. Typically, the (SiO₃) units form single chains by sharing an oxygen atom of the SiO₄ tetrahedra, and the single chains repeat their tetrahedral growth or translation pattern in multiples of three forming wollastonite, calcite or enstalite.

A reaction in forming the phosphor at high temperature is considered to be, in a number of embodiments of the invention, the crystallization of silica into cristobalite, while incorporating activators Eu²⁺ and/or Mn²⁺ in the crystals. This reaction is supported by a medium that at the firing temperature is liquid. In other words, by a “flux”. There are other types of metal silicates that can be molten in the temperature range for the crystallization. These silicates can function as flux providing the fluid medium at the temperatures of, for example, ˜900 to ˜1300° C.

Synthesis can, for example, include: (1) mixing appropriate precursors (e.g., the metal carbonates and/or metal nitrates and/or metal oxides, and/or metal halides—such as fluorides, and/or a source of halide X), where at some point in the mixing a slurry can be used to ensure the intimate contact of the reactant ingredients ready for the solid-state chemical reactions; (2) optionally milling the mixture to achieve further contact at a fine particle level of the inorganic solids; (3) optionally drying the mixed material, (4) optionally heating under a reducing gas, such as, for example, hydrogen at a given first temperature, (5) optionally mixing in further precursor of X, (6) firing at a temperature higher than the given first temperature, under a reducing gas, (7) optionally washing the phosphor with a solvent effective to wash out unreacted ingredients, and (8) optionally applying a post formation treatment such as sieving or size separation.

It will be recognized that the materials provided in the forming reaction may not altogether convert to the forms of formula I, and that all unreacted materials may not wash out (if a washing step is used). However, it is believed that formula I describes the significant hosting and flux providing phases of the phosphor.

The first temperature can be at, for example, 700 to 1100° C. For example, it can be a range from 700° C., 710° C., 720° C., 730° C., 740° C., 750° C., 760° C., 770° C., 780° C., 790° C., 800° C., 810° C., 820° C., 830° C., 840° C., 850° C., 860° C., 870° C., 880° C., 890° C., 900° C., 910° C., 920° C., 930° C., 940° C., 950° C., 960° C., 970° C., 980° C., 990° C., 1000° C., upwards. Or a range from 1100° C., 1090° C., 1080° C., 1070° C., 1060° C., 1050° C., 1040° C., 1030° C., 1020° C., 1010° C., 1000° C., 990° C., 980° C., 970° C., 960° C., 950° C., 940° C., 930° C., 920° C., 910° C., 900° C., 890° C., 880° C., 870° C., 860° C., 850° C., 840° C., 830° C., 820° C., 810° C., 800° C. downwards.

The firing can be at, for example, 900 to 1300° C. For example, it can be a range from 900° C., 910° C., 920° C., 930° C., 940° C., 950° C., 960° C., 970° C., 980° C., 990° C., 1000° C., 1010° C., 1020° C., 1030° C., 1040° C., 1050° C., 1060° C., 1070° C., 1080° C., 1090° C., 1100° C., 1110° C., 1120° C., 1130° C., 1140° C., 1150° C., 1160° C., 1170° C., 1180° C., 1190° C., or 1200° C., upwards. Or a range from 1300° C., 1290° C., 1280° C., 1270° C., 1260° C., 1250° C., 1240° C., 1230° C., 1220° C., 1210° C., 1200° C., 1190° C., 1180° C., 1170° C., 1160° C., 1150° C., 1140° C., 1130° C., 1120° C., 1110° C., 1100° C., 1090° C., 1080° C., 1070° C., 1060° C., 1050° C., 1040° C., 1030° C., 1020° C., 1010° C. or 1000° C. downwards. The firing can be, for example, at a temperature 40° C. or more, 50° C. or more, 60° C. or more, 70° C. or more, 48° C. or more, 90° C. or more, or 100° C. or more higher than the flux temperature.

In certain embodiments, the SiO₂ component is substantially 0% cristobolite, and the rest amorphous or quartz, or a given molar percent or more cristobolite, and the rest amorphous or quartz. The given percent can be, for example, 1, 2, 3, 4, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95 or 100%. Or, SiO₂ component can be a given percentage or less cristobolite. The second given percent can be, for example, 1, 2, 3, 4, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90 or 95%.

In certain embodiments x is substantially 1. In other embodiments, x is substantially 0. In certain embodiments z is substantially 0. In certain embodiments, z=0, and x or y is 0.50 or less, 0.49 or less, 0.48 or less, 0.47 or less, 0.46 or less, and so on by 0.01 increments to 0.01 or less. In certain embodiments x or y or z is 0.50 or less, 0.49 or less, 0.48 or less, 0.47 or less, 0.46 or less, and so on by 0.01 increments to 0.01 or less.

In certain embodiments, the quantum efficiency of phosphors of the invention is 40% or more.

The emission peak of metal silicate-silica-based, polymorphous phosphors of the invention is measured with the excitation source being light at 300-500 nm±10 nm. In certain embodiments, the emission peak range is from one of the following lower endpoints (inclusive) or from one of the following upper endpoints (inclusive). The lower endpoints are 360, 361, 362, 363, and each one nm increment up to 799 nm. The upper endpoints are 800, 799, 798, 797, and each one nm down to 361.

In some embodiments, the lower endpoints are 430, 431, 432, and each one nm increment up to 489 nm. In some embodiments, the upper endpoints are 490, 489, 488, and each one nm increment down to 431 nm.

In some embodiments, the lower endpoints are 500, 501, 502, and each one nm increment up to 559 nm. In some embodiments, the upper endpoints are 560, 559, 558, and each one nm increment down to 501 nm.

In some embodiments, the lower endpoints are 590, 591, 592, and each one nm increment up to 659 nm. In some embodiments, the upper endpoints are 660, 659, 658, and each one nm increment down to 591 nm.

In certain embodiments, the phosphor is effectively excited (sufficiently for use with a corresponding semiconductor light emitting device) with light of wavelength from 400 to 420 nm.

Rε is substantially composed of all Eu or Mn or both, but minor amounts, such as 4% or less, 2% or less, 1% or less, 0.5% or less, 0.4% or less, 0.3% or less, 0.2% or less, or 0.1% or less of activators, may be other activator(s).

Among candidate metal ions M, ions of Mg and Ba are less preferred. In certain embodiments, M is 99% (molar) or more, 99.1% or more, 99.5% or more, 99.7% or more, 99.8% or more, 99.8% or more, or 99.9% or more of one metal (such as, for example, Ca).

In certain embodiments, the phosphor is according to (CaSiO₃).(SiO₂):Eu²⁺, Mn²⁺, I⁻, with the concentration and ratio of Eu²⁺ and Mn²⁺ selected to provide a peak emission between 600 nm and 640 nm or 620 nm and 660 nm (or an included range to one of the foregoing ranges), and a chromaticity of x=0.62±0.06, y=0.30±0.06.

In certain embodiments, the phosphor is according to (CaSiO₃).(SiO₂):Eu²⁺, I⁻, with the concentration of Eu²⁺ selected to provide a peak emission between 445 nm and 480 nm or 455 nm and 475 nm or 445 nm and 475 nm (or an included range to one of the foregoing ranges), and a chromaticity of x=0.20±0.06, y=0.10±0.06.

In certain embodiments, the phosphor is according to (CaSiO₃).(SiO₂):Eu²⁺, Mn²⁺, Cl⁻, with the concentration and ratio of Eu²⁺ and Mn²⁺ selected to provide a chromaticity of x=0.40±0.06, y=0.20±0.06.

When used in a lighting device, it will be recognized that the phosphors can be excited by light from a primary source, such as an semiconductor light source emitting in the wavelength of 300˜420 nm, or from secondary light such as emissions from other phosphor(s) emitting in the same wavelength range. Where the excitation light is secondary, in relation to the phosphors of the invention, the excitation-induced light is the relevant source light. Devices that use the phosphor of the invention can include mirrors, such as dielectric mirrors, to direct light produced by the phosphors to the light output rather than the interior of the device (such as the primary light source).

The semiconductor light source can, in certain embodiments, emit light of 300 nm or more, or 305 nm or more, or 310 nm or more, and so on in increments of 5 nm to 400 nm or more. The semiconductor light source can, in certain embodiments, emit light of 420 nm or less, or 415 nm or less, or 410 nm or less, and so on in increments of 5 nm to 350 nm or less.

Phosphor particles may be dispersed in the lighting device with a binder or solidifier, dispersant (i.e., light scattering material), filler or the like, The binder can be, for example, a light curable polymer such as an acrylic resin, an epoxy resin, polycarbonate resin, a silicone resin, glass, quartz and the like. The phosphor can be dispersed in the binder by methods known in the art. For example, in some cases the phosphor can be suspended in a solvent, and the polymer suspended, dissolved or partially dissolved in the solvent, the slurry dispersed on the lighting device, and the solvent evaporated. In some cases, the phosphor can be suspended in a liquid, pre-cured precursor to the resin, the slurry dispersed, and the polymer cured. Curing can be, for example, by heat, UV, or a curing agent (such as a free radical initiator) mixed in the precursor. Or, in another example, the binder may be liquefied with heat, a slurry formed, and the slurry dispersed and allowed to solidify in situ. Dispersants include, for example, titanium oxide, aluminum oxide, barium titanate, silicon dioxide, and the like.

It is anticipated that lighting devices of the invention will use semiconductor light sources such as LEDs to either create excitation energy, or excite another system to provide the excitation energy for the phosphors. Devices using the invention can include, for example, white light producing lighting devices, indigo light producing lighting devices, blue light producing lighting devices, green light producing lighting devices, yellow light producing lighting devices, orange light producing lighting devices, pink light producing lighting devices, red light producing lighting devices, or lighting devices with an output chromaticity defined by the line between the chromaticity of a phosphor of the invention and that of one or more second light sources. Headlights or other navigation lights for vehicles can be made with the devices of the invention. The devices can be output indicators for small electronic devices such as cell phones and PDAs. The lighting devices can also be the backlights of the liquid crystal displays for cell phones, PDAs and laptop computers. Given appropriate power supplies, room lighting can be based on devices of the invention. The warmth (i.e., amount of yellow/red chromaticity) of lighting devices can be tuned by selection of the ratio of light from phosphor of the invention to light from a second source.

Suitable semiconductor light sources are any that create light that excites the phosphors, or that excites a phosphor that in turn excites the phosphors of the invention. Such semiconductor light sources can be, for example, Ga—N type semiconductor light sources, In—Al—Ga—N type semiconductor light sources, and the like. In some embodiments, blue or near UV emitting semiconductor light sources are used.

For a semiconductor light source having a using at least two different phosphors, it can be useful to disperse the phosphors separately, and superimpose the phosphor layers instead of dispersing the phosphors together in one matrix. Such layering can be used to obtain a final light emission color by way of a plurality of color conversion processes. For example, the light emission process is: absorption of the semiconductor light source light emission by a first phosphor, light emission by the first phosphor, absorption of the light emission of the first phosphor by a second phosphor, and the light emission by the second phosphor.

FIG. 15 shows an exemplary layer structure of a semiconductor light source. The blue semiconductor light comprises a substrate Sb, for example, a sapphire substrate. For example, a buffer layer B, an n-type contact layer NCt, an n-type cladding layer NCd, a multi-quantum well active layer MQW, a p-type cladding layer PCd, and a p-type contact layer PCt are formed in that order as nitride semiconductor layers. The layers can be formed, for example, by organometallic chemical vapor deposition (MOCVD), on the substrate Sb. Thereafter, a light-transparent electrode LtE is formed on the whole surface of the p-type contact layer PCt, a p electrode PEI is formed on a part of the light-transparent electrode LtE, and an n electrode NEI is formed on a part of the n-type contact layer NCt. These layers can be formed, for example, by sputtering or vacuum deposition.

The buffer layer B can be formed of, for example, AlN, and the n-type contact layer NCt can be formed of, for example, GaN.

The n-type cladding layer NCd can be formed, for example, of Al_(r)Ga_(1-r)N wherein 0≦r<1, the p-type cladding layer PCd can be formed, for example, of Al_(q)Ga_(1-q)N wherein 0<q<1, and the p-type contact layer PCt can be formed, for example, of Al_(s)Ga_(1-s)N wherein 0≦s<1 and s<q. The band gap of the p-type cladding layer PCd is made larger than the band gap of the n-type cladding layer NCd. The n-type cladding layer NCd and the p-type cladding layer PCd each can have a single-composition construction, or can have a construction such that the above-described nitride semiconductor layers having a thickness of not more than 100 angstroms and different from each other in composition are stacked on top of each other so as to provide a superlattice structure. When the layer thickness is not more than 100 angstroms, the occurrence of cracks or crystal defects in the layer can be prevented.

The multi-quantum well active layer MQW can be composed of a plurality of InGaN well layers and a plurality of GaN barrier layers. The well layer and the barrier layer can have a thickness of not more than 100 angstroms, preferably 60 to 70 angstroms, so as to constitute a superlattice structure. Since the crystal of InGaN is softer than other aluminum-containing nitride semiconductors, such as AlGaN, the use of InGaN in the layer constituting the active layer MQW can offer an advantage that all the stacked nitride semiconductor layers are less likely to crack. The multi-quantum well active layer MQW can also be composed of a plurality of InGaN well layers and a plurality of AlGaN barrier layers. Or, the multi-quantum well active layer MQW can be composed of a plurality of AlInGaN well layers and a plurality of AlInGaN barrier layers. In this case, the band gap energy of the barrier layer can be made larger than the band gap energy of the well layer.

A reflecting layer can be provided on the substrate Sb side from the multi-quantum well active layer MQW, for example, on the buffer layer B side of the n-type contact layer NCt. The reflecting layer can also be provided on the surface of the substrate Sb remote from the multi-quantum well active layer MQW stacked on the substrate Sb. The reflecting layer can have a maximum reflectance with respect to light emitted from the active layer MQW and can be formed of, for example, aluminum, or can have a multi-layer structure of thin GaN layers. The provision of the reflecting layer permits light emitted from the active layer MQW to be reflected from the reflecting layer, can reduce the internal absorption of light emitted from the active layer MQW, can increase the quantity of light output toward above, and can reduce the incidence of light on the mount for the light source to prevent a deterioration.

Shown in FIGS. 13-14 are some exemplary semiconductor light source-phosphor structures. FIG. 13 shows a light emitting device 10 with an semiconductor light source chip 1 powered by leads 2, and having phosphor-containing material 4 secured between the semiconductor light source chip and the light output 6. A reflector 4 can serve to concentrate light output. A transparent envelope 5 can isolate the semiconductor light source and phosphor from the environment and/or provide a lens. The lighting device 20 of FIG. 14 is a panel device having multiple semiconductor light source chips 11, leads 12, subsidiary leads 12′, phosphor-containing material 14, and transparent envelope 15.

It will be understood by those of ordinary skill in the art that there are any number of ways to associate phosphors with an semiconductor light source such that light from the semiconductor light source is managed by its interaction with the phosphors. U.S. Patent Applications 2004/0145289 and 2004/0145288 illustrate lighting devices where phosphor is positioned away from the light output of the semiconductor light sources. U.S. Patent Applications 2004/01450307 and 2004/0159846 further illustrate, without limitation, lighting devices that can be used in the invention.

Semiconductor light source-based white light devices can be used, for example, in a self-emission type display for displaying a predetermined pattern or graphic design on a display portion of an audio system, a household appliance, a measuring instrument, a medical appliance, and the like. Such semiconductor light source-based light devices can also be used, for example, as light sources of a back-light for LCD displays, a printer head, a facsimile, a copying apparatus, and the like.

Among the additional phosphors that can be mixed with phosphors of the invention, some of those believed to be useful include those identified above in the initial paragraphs of this specification.

Among the additional phosphors that can be mixed with phosphors of the invention, some of those believed to be useful include: Y₃Al₅O₁₂:Ce³⁺ (YAG), Lu₃Ga₂(AlO₄)₃:Ce³⁺; La₃In₂(AlO₄)₃:Ce³⁺; Ca₃Ga₅BaYSiAlO₁₂:Ce³⁺; CaGa₂S₄:Eu²⁺; SrCaSiO₄:Eu²⁺; ZnS:Cu, CaSi₂O₂N:Eu²⁺; SrSi₂O₂N:Eu²⁺; SrSiAl₂O₃N₂:Eu²⁺; Ba₂MgSi₂O₇:Eu²⁺; Ba₂SiO₄:Eu²⁺; La₂O₃.11Al₂O₃:Mn²⁺; Ca₈Mg(SiO₄)₄Cl₄:Eu²⁺,Mn²⁺; (CaM)(Si,Al)₁₂(O,N)₁₆:Eu²⁺,Tb³⁺,Yb³⁺; YBO₃:Ce³⁺,Tb³⁺; BaMgAl₁₀O₁₇:Eu²⁺, Mn²⁺; (Sr,Ca,Ba)(Al,Ga)₂S₄:Eu²⁺; BaCaSi₇N₁₀:Eu²⁺; (SrBa)₃MgSi₂O₈:Eu²⁺; (SrBa)₂P₂O₇:Eu²⁺; (SrBa)₂Al₁₄O₂₅:Eu²⁺; LaSi₃N₅:Ce³⁺; (BaSr)MgAl₁₀O₁₇:Eu²⁺;

Temperatures described herein for synthetic processes involving a substantial gas phase are of the oven or other reaction vessel in question, not of the reactants per se.

“White” light is light that of certain chromaticity values (known and well published in the art).

The following examples further illustrate the present invention, but of course, should not be construed as in any way limiting its scope.

EXAMPLE 1a Preparation of CaSiO₃.(SiO₂)_(n): Eu²⁺, Mn²⁺, I

1.14 g of Eu₂O₃, (0.65 mole %), 3.9 g of CaO (7 mole %), 0.78 g of CaF₂ (1 mole %), 0.115 g of MnCO₃ (0.1 mole %), 60.08 g of silicic acid (100 mole %) and 21 g of NH₄I (14.4 mole %) were mixed in dry powder form. The mixed powder was further dried in dry nitrogen at 140° C. for 4 hours. The powder was then fired at 900° C. in forming gas (5% v/v H₂ in N₂) for 1 hour. After the material cooled down, 14 g of NH₄I was added and mixed again. The mixed powder was fired at 1000° C. in forming gas for 1 hour. The phosphor obtained was (CaSiO₃).(SiO₂):Eu²⁺, Mn²⁺, I⁻. The silica, SiO₂, was in cristobalite form and the calcium inosilicate is in the Wollastonite form, as evidenced by X-ray diffraction pattern shown in FIG. 3 (shown relative to Wollastonite inosiliate, to quartz, and to cristobalite silica). The phosphor emitted bright red light peaking at 635 nm upon 410 nm light excitation, as shown in FIG. 1. The long term stability (longevity) of the phosphor when subjected to 85° C. and 85% relative humidity is shown in FIG. 2.

EXAMPLE 1b-f Preparation of CaSiO₃.(SiO₂)_(n): Eu²⁺, Mn²⁺, I

The method of Example 1a was used, except that the ratio of Eu²⁺ and Mn²⁺ were varied to obtain the following phosphors: [Eu²⁺], [Mn²⁺], Emitting Phosphor Formula mol % mol % Color b (CaSiO₃).(SiO₂):Eu²⁺, Mn²⁺, I⁻. 0.65 0.05 Pink c (CaSiO₃).(SiO₂):Eu²⁺, Mn²⁺, I⁻. 0.65 0.1 Pink d (CaSiO₃).(SiO₂):Eu²⁺, Mn²⁺, I⁻. 0.65 0.15 Pink e (CaSiO₃).(SiO₂):Eu²⁺, Mn²⁺, I⁻. 0.65 0.2 Red f (CaSiO₃).(SiO₂):Eu²⁺, Mn²⁺, I⁻. 0.65 0.5 Red

EXAMPLE 2 Preparation of CaSiO₃.(SiO₂)_(n): Eu²⁺, Mn²⁺, Cl

Mix 1.14 g of Eu₂O₃, (0.65 mole %), 3.9 g of CaO (7 mole %), 0.78 g of CaF₂ (1 mole %), 0.115 g of MnCO₃ (0.1 mole %), 60.08 g of silicic acid (100 mole %) and 14 g of NH₄Cl (26 mol %) by dry grinding. The mixed powder is further dried in dry nitrogen at 140° C. for 4 hours. The powder is then fired at 900° C. in dry nitrogen for 1 hour. After the material cools down to room temperature, 14 g of NH₄Cl were added and the material mixed once again. The mixed powder was then fired at 1000° C. in forming gas for 1 hour. The phosphor obtained was CaSiO₃.(SiO₂)_(n): Eu²⁺, Mn²⁺, Cl⁻. The phosphor emitted bright orange-red light peaking at 422 nm and 585 nm upon 410 mm light excitation, as shown in FIG. 4.

EXAMPLE 3a Preparation of CaSiO₃.(SiO₂)_(n): Eu²⁺, I

1.14 g of Eu₂O₃, (0.65 mole %), 3.9 g of CaO (7 mole %), 0.78 g of CaF₂ (1 mole %), 60.08 g of silicic acid (100 mole %) and 14 g of NH₄I (9.6 mole %) was mixed in dry powder form. The mixed powder was further dried in nitrogen at 140° C. for 4 hours. The powder was then fired at 900° C. in dry nitrogen for 1 hour. After the material cooled down, 14 g of NH₄I was added and mixed again. The mixed powder was fired at 1000° C. in forming gas for 1 hour. The phosphor obtained was CaSiO₃.(SiO₂)_(n): Eu²⁺, I⁻, and emitted bright blue light peaking at 465 n upon 410 nm light excitation, as shown in FIG. 5. The phosphor showed polymorphous crystalline composition with wollastonite of CaSiO₃ and cristobalite SiO₂. Longevity is shown in FIG. 6.

EXAMPLE 3b-i Preparation of CaSiO₃.(SiO₂)_(n): Eu²⁺, I

The method of Example 3a was used, except that the ratio of Eu²⁺ and Mn²⁺ were varied to obtain the following phosphors: [Eu²⁺], Phosphor Formula mol % Emitting Peak, nm b (CaSiO₃).(SiO₂):Eu²⁺, I⁻ 0.25 466 c (CaSiO₃).(SiO₂):Eu²⁺, I⁻ 0.45 465 d (CaSiO₃).(SiO₂):Eu²⁺, I⁻ 0.65 465 e (CaSiO₃).(SiO₂):Eu²⁺, I⁻ 0.85 466 f (CaSiO₃).(SiO₂):Eu²⁺, I⁻ 1.2 466 g (CaSiO₃).(SiO₂):Eu²⁺, I 1.5 466 h (CaSiO₃).(SiO₂):Eu²⁺, I 2.0 465 i (CaSiO₃).(SiO₂):Eu²⁺, I 3.0 465

EXAMPLE 4 Preparation of CaSiO₃.(SiO₂)_(n): Eu²⁺, Mn²⁺, Br

1.14 g of Eu₂O₃, (0.65 mole %), 3.9 g of CaO (9.7 mole %), 0.78 g of CaF₂ (1 mole %), 0.115 g of MnCO₃ (0.1 mole %), 60.08 g of silicic acid (100 mole %) and 16 g of NH₄Br (16 mole %) was mixed by dry grinding. The mixed powder was further dried in dry nitrogen at 140° C. for 4 hours. The powder was then fired at 900° C. in forming gas for 1 hour. After the material cooled down, 14 g of NH₄Br was added and mixed again. The mixed powder was fired at 1000° C. in forming gas for 1 hour. The phosphor obtained was CaSiO₃.(SiO₂)_(n): Eu²⁺, Mn²⁺, Br⁻, and emitted bright blue light (430 m) and orange light (584 nm) upon 400 nm light excitation, as shown in FIG. 7.

EXAMPLE 5 Preparation of MgSiO₃.(SiO₂)_(n): Eu²⁺, Mn²⁺,I⁻

1.14 g of Eu₂O₃, (0.65 mole %), 3.9 g of MgO (7 mole %), 0.115 g of MnCO₃ (0.1 mole %), 60.08 g of silicic acid (100 mole %) and 14 g of NH₄I (15 mole %) were mixed in dry powder form. The mixed powder was further dried in dry nitrogen at 140° C. for 4 hours. The powder was then fired at 900° C. in forming gas for 1 hour. After the material cooled down, 14 g of NH₄I was added and mixed again. The mixed powder was fired at 1000° C. in dry forming for 1 hour. The phosphor obtained was ([Mg]SiO₃).(SiO₂)_(n):Eu²⁺, Mn²⁺, I⁻. The silica, SiO₂, is crystallized in cristobalite form and the magnesium inosilicate is in the enstalite form, as evidenced by X-ray diffraction pattern shown in FIG. 9 (shown relative to Enstalite Mg and to quartz). This diffraction pattern shows the silica is largely amorphous. This phosphor emitted upon 410 nm light excitation as shown in FIG. 8 (blue at 430 nm and red at 644 nm).

EXAMPLE 6 Preparation of MgSiO₃.(SiO₂)_(n): Eu²⁺, Mn²⁺, Br⁻

1.14 g of Eu₂O₃, (0.65 mole %), 3.9 g of MgO (7 mole %), 0.115 g of MnCO₃ (0.1 mole %), 60.08 g of silicic acid (100 mole %) and 16 g of NH₄Br (16.3 mole %) was mixed by dry grinding. The mixed powder was further dried in dry nitrogen at 140° C. for 4 hours. The powder was then fired at 900° C. in forming gas for 1 hour. After the material cooled down, 14 g of NH₄Br was added and mixed again. The mixed powder was fired at 1000° C. in forming gas for 1 hour. The phosphor obtained was MgSiO₃ (SiO₂)_(n):Eu²⁺, Mn²⁺ Br⁻, and emitted upon 400 nm light excitation as shown in FIG. 10 (blue at 410 nm, blue at 475 nm and red at 620 nm).

EXAMPLE 7 Preparation of CaSiO₃:Eu²⁺,Mn²⁺,I⁻

1.14 g of Eu₂O₃, (0.65 mole %), 3.9 g of CaO (7 mole %), 0.78 g of CaF₂ (1 mole %), 0.115 g of MnCO₃ (0.1 mole %), 60.08 g of silicic acid (100 mole %) and 16 g of NH₄I (11 mole %) was mixed by dry grinding. The mixed powder was further dried in dry nitrogen at 140° C. for 4 hours. The powder was then fired at 900° C. in forming gas for 1 hour. After the material cooled down, 14 g of NH₄I was added and mixed again. The mixed powder was fired at 1000° C. in forming gas for 1 hour. The phosphor obtained was CaSiO₃:Eu²⁺, Mn²⁺, I⁻, and emitted upon 400 nm light excitation, as shown in FIG. 11 (blue at 460 nm and red at 610 nm).

EXAMPLE 8 Preparation of (SiO₂)_(n):Eu²⁺, Mn²⁺, I⁻

1.14 g of Eu₂O₃, (0.65 mole %), 0.78 g of CaF₂ (1 mole %), 0.115 g of MnCO₃ (0.1 mole %), 60.08 g of silicic acid (100 mole %) and 16 g of NH₄I (11 mole %) was mixed by dry grinding. The mixed powder was further dried in dry nitrogen at 140° C. for 4 hours. The powder was then fired at 900° C. in forming gas for 1 hour. After the material cooled down, 14 g of NH₄Br was added and mixed again. The mixed powder was fired at 1000° C. in forming gas for 1 hour. The phosphor obtained was (SiO₂)_(n):Eu²⁺, Mn²⁺, I⁻, and emitted upon 400 nm light excitation as shown in FIG. 12 (blue at 430 nm and red at 640 nm).

EXAMPLE 9 Making a White Light Device with 410 nm-Emitting LED Chip and a First Phosphor Blend

The phosphor blend is made of a red emitting metal silicate-silica-based, polymorphous phosphor CaSiO₃.(SiO₂)_(n): Eu²⁺, Mn²⁺, I⁻ as made in the Example 1, a green-emitting phosphor, BaMgAl₁₀O₁₇:Eu²⁺,Mn²⁺ (BAM:Eu, Mn) (G) and a blue-emitting phosphor CaSiO₃.(SiO₂)_(n): Eu²⁺, I⁻ (B) as made in the Example 3. Mix the three phosphors with appropriate weight ratios and further mix the phosphor blend with epoxy resin to form a slurry. Apply the slurry onto an InGaN-based LED chip that emits at 410 nm. The device generates light with white color whose color coordinates can be varied by changing the ratio of the three phosphors.

EXAMPLE 10 Making a White Light Device with 410 nm-Emitting LED Chip and a Second Phosphor Blend

The phosphor blend is made of a red emitting metal silicate-silica-based, polymorphous phosphor CaSiO₃.(SiO₂)_(n): Eu²⁺, Mn²⁺, I⁻ as made in the Example 1, a green-emitting phosphor, SrGa₂S₄:Eu²⁺ (STG:Eu) (G) and a blue-emitting phosphor CaSiO₃.(SiO₂)_(n): Eu²⁺, I⁻ (B) as made in the Example 3. Mix the three phosphors with appropriate weight ratios and further mix the phosphor blend with epoxy resin to form a slurry. Apply the slurry onto an InGaN-based LED chip that emits at 410 nm. The device generates light with white color whose color coordinates can be varied by changing the ratio of the three phosphors. The device architecture can be as in FIG. 13

EXAMPLE 11 Making a Purple Light Device with 410 nm-Emitting LED Chip and a Purple-Emitting Phosphor

A single phosphor, the purple-emitting CaSiO₃.(SiO₂)_(n): Eu²⁺, Mn²⁺, Cl⁻ as made in the Example 2 is mixed with epoxy resin to form a slurry. The slurry is applied onto an InGaN-based LED chip that emits at 410 nm. The device generates light with purple color. This light color is suitable for certain lighting in entertainment environment.

Publications and references, including but not limited to patents and patent applications, cited in this specification are herein incorporated by reference in their entirety in the entire portion cited as if each individual publication or reference were specifically and individually indicated to be incorporated by reference herein as being fully set forth. Any patent application to which this application claims priority is also incorporated by reference herein in the manner described above for publications and references.

While this invention has been described with an emphasis upon preferred embodiments, it will be obvious to those of ordinary skill in the art that variations in the preferred devices and methods may be used and that it is intended that the invention may be practiced otherwise than as specifically described herein. Accordingly, this invention includes all modifications encompassed within the spirit and scope of the invention as defined by the claims that follow. 

1. A light emitting device comprising: a semiconductor light source producing light output including wavelengths of 300 nm or more; and a wavelength manager located between the light source and the light output for the device, comprising a phosphor according to the formula: [(BvSiO₃)_(x)(Mv₂SiO₃)_(y)(Tv₂(SiO₃)₃)_(z)]_(m).(SiO₂)_(n):Rε, X  (I) wherein x, y and z are any value such that x+y+z=1; By is one or more divalent alkaline earth metals; Mv is one or more monovalent alkaline metals; Tv is one or more trivalent metal ions; Rε is one or more activators selected from Eu²⁺ and Mn²⁺; X is one or more halides; m is 1 or 0; and (i) n>3 if m=1 and provides an amount of silica effective to host useful luminescence or (ii) n=1 if m=0. 2-9. (canceled)
 10. The light emitting device of claim 1, wherein the wavelength manager comprises one or more additional phosphors, the one or more additional phosphors adjusting light produced by the device.
 11. The light emitting device of claim 10, wherein the wavelength manager changes the light output to white light.
 12. A light emitting device according to claim 1, wherein: the semiconductor light source comprises a double hetero structure comprising a light emitting layer sandwiched between a p-type clad layer and an n-type clad layer.
 13. A light emitting device according to claim 12, wherein: the p-type clad layer is formed of Al_(q)Ga_(1-q)N where 0<q<1, and the n-type clad layer is formed of Al_(r)Ga_(1-r)N where 0≦r<1; and/or the band gap of the p-type clad layer is larger than that of the n-type clad layer.
 14. A light emitting device according to claim 1, wherein: the semiconductor light source comprises a light emitting layer containing indium and comprising a quantum well structure.
 15. A light emitting device according to claim 14, wherein: the quantum well structure comprises a well layer of InGaN and a barrier layer of GaN; and/or the quantum well structure comprises a well layer of InGaN and a barrier layer of AlGaN; and/or the quantum well structure comprises a well layer of AlInGaN and a barrier layer of AlInGaN, and the band gap energy of the barrier layer is larger than that of the well layer; and/or wherein: the well layer has a thickness of not more than 100 angstroms.
 16. A light emitting device according to claim 1, wherein the semiconductor light source comprises a single well light emitting element.
 17. A light emitting device according to claim 1, wherein the semiconductor light source comprises multiple light emitting elements on a substrate. 18-26. (canceled)
 27. A method of making a light emitting device according to claim 1, comprising associating the phosphor with the semiconductor light source so that the light emission of the device is modified by the associated phosphor.
 28. A phosphor according to the formula: [(BvSiO₃)_(x)(Mv₂SiO₃)_(y)(Tv₂(SiO₃)₃)_(z)]_(m).(SiO₂)_(n):Rε, X  (I) wherein x, y and z are any value such that x+y+z=1; By is one or more divalent alkaline earth metals; Mv is one or more monovalent alkaline metals; Tv is one or more trivalent metal ions; Rε is one or more activators selected from Eu²⁺ and Mn²⁺; X is one or more halides; m is 1 or 0; and (i) n>3 if m=1 and provides an amount of silica effective to host useful luminescence or (ii) n=1 if m=0.
 29. The phosphor of claim 28, wherein Mv comprises one or more ions of Li, Na or K.
 30. The phosphor of claim 28, wherein Bv comprises one or more divalent alkaline earth metals.
 31. The phosphor of claim 30, wherein By comprises one or more divalent ions of Ca or Sr.
 32. The phosphor of claim 28, wherein Bv comprises one or more divalent ions of Be, Mg, Ca, Sr, Ba, Mn, Co, Ni, Cu, Zn, Cd or Hg.
 33. The phosphor of claim 28, wherein Tv comprises one or more trivalent ions of Al, Ga, In, Sc, Y or La.
 34. The phosphor of claim 28, wherein Rε comprises substantially all Eu²⁺.
 35. The phosphor of claim 28, wherein Rε comprises substantially all Mn²⁺.
 36. The phosphor of claim 28, wherein Rε comprises substantially all Eu²⁺ and Mn²⁺.
 37. The phosphor of claim 28, wherein the phosphor is according to (CaSiO₃).(SiO₂):Eu²⁺, Mn²⁺, I⁻, with the concentration and ratio of Eu²⁺ and Mn²⁺ selected provide a peak emission between 620 nm and 660 nm, and a chromaticity of x=0.62±0.06, y=0.30±0.06.
 38. The phosphor of claim 28, wherein the phosphor is according to (CaSiO₃).(SiO₂):Eu²⁺, I⁻, with the concentration of Eu²⁺ selected to provide a peak emission between 445 nm and 480 nm, and a chromaticity of x=0.20±0.06, y=0.10±0.06.
 39. The phosphor of claim 28, wherein the phosphor is according to (CaSiO₃).(SiO₂):Eu²⁺, Mn²⁺, Cl⁻, with the concentration and ratio of Eu²⁺ and Mn²⁺ selected to provide a chromaticity of x=0.40±0.06, y=0.20±0.06.
 40. A phosphor of claim 28, wherein the phosphor comprises metal silicate in wollastonite form and silica in cristobalite form.
 41. A phosphor of claim 28, wherein the phosphor comprises metal silicate in calcite form and silica in cristobalite form.
 42. A phosphor of claim 28, wherein the phosphor comprises metal silicate in enstalite form and silica in cristobalite form.
 43. A phosphor of claim 28, wherein the mole percentage of X is 5% or less of SiO₂
 44. A method of making a phosphor according to the formula: [(BvSiO₃)_(x)(Mv₂SiO₃)_(y)(Tv₂(SiO₃)₃)_(z)]_(m).(SiO₂)_(n):Rε, X  (I) wherein x, y and z are any value such that x+y+z=1; By is one or more divalent alkaline earth metals; Mv is one or more monovalent alkaline metals; Tv is one or more trivalent metal ions; Rε is one or more activators selected from Eu²⁺ and Mn²⁺; X is one or more halides; m is 1 or 0; and (i) n>3 if m=1 and provides an amount of silica effective to host useful luminescence or (ii) n=1 if m=0, comprising: providing an appropriate mixture of precursors optionally including a halide source; and firing the product of the first heating at a temperature from 900° C. to 1300° C. under a reducing atmosphere and in the presence of a halide source, wherein one or more of the following applies: the process further comprises, prior to the firing, heating the appropriate mixture, optionally including a halide source, at a temperature from 700° C. to 1100° C. under a reducing atmosphere, where the heating is at a temperature lower than that of the firing, or the mole percentage of X in the phosphor product is 5% or less of SiO₂.
 45. The method of claim 44, further comprising, prior to the firing, heating the appropriate mixture, optionally including a halide source, at a temperature from 700° C. to 1100° C. under a reducing atmosphere, where the heating is at a temperature lower than that of the firing.
 46. The method of claim 45, wherein a halide source is present in the heating. 